Titel:
|
|
In-situ doping and local overcompensation of high performance LPCVD polysilicon passivated contacts as approach to industrial IBC cells
|
|
|
|
Auteur(s):
|
|
|
|
|
|
Gepubliceerd door:
|
Publicatie datum:
|
|
ECN
Zonne-energie
|
10-8-2016
|
|
|
|
ECN publicatienummer:
|
Publicatie type:
|
|
ECN-W--16-024
|
Artikel wetenschap tijdschrift
|
|
|
|
Aantal pagina's:
|
|
|
7
|
|
Gepubliceerd in: Energy Procedia (Elsevier), , 2016, Vol.92, p.427-433.
Samenvatting:
In this work, we investigate polysilicon passivation contacts, to be used for high performance IBC cells. We demonstrate an LPCVD process for in-situ p-type doped polysilicon. The p-type polysilicon can be locally overcompensated to n-type polysilicon using phosphorous implantation or POCl3 diffusion. Both contacts show excellent surface passivation, with recombination current (Jo) of 12 fA/cm2 for p-poly on a polished Si surface, and less than 10 fA/cm2 for compensated n-poly both on textured and polished surfaces. These polysilicon layers are implemented in the fabrication of n-PERT cells with front and rear polysilicon contacts. The resulting textured half-fabricated cells have an implied Voc of 701 mV after hydrogenation via PECVD deposition of SiNx:H. Different metallization processes, relevant for IBC cells, are applied. A Voc of 685 mV is obtained for the best cell metallized with low-temperature metallization (ITO/low-temperature Ag paste), and 678 mV is obtained for the best cell with industrial screen-printed firing-through contacts. In these n-PERT cells the same thin oxide layer is used for p-type and n-type polysilicon contacts.
Meer Informatie:
Terug naar overzicht.