Publicaties

Skip Navigation Links.
Recent verschenen
Expand per documenttypeper documenttype
Collapse per Unitper Unit
Expand Business DevelopmentBusiness Development
Expand Biomass & Energy EfficiencyBiomass & Energy Efficiency
Expand BeleidsstudiesBeleidsstudies
Expand Corporate CommunicationsCorporate Communications
Expand CorporateCorporate
Expand Environment & Energy EngineeringEnvironment & Energy Engineering
Expand Program DevelopmentProgram Development
Expand Quality Safety Health and EnvironmentQuality Safety Health and Environment
Expand Strategy & PlanningStrategy & Planning
Expand WindenergieWindenergie
Collapse Zonne-energieZonne-energie
2018
2017
2016
2015
2014
2013
2012
2011
2010
2009
2008
2007
2006
2005
2004
2003
2002
2001
2000
1999
1998
1997
Expand per Clusterper Cluster

Zoeken naar publicaties:
Beperk het zoeken tot de velden:

ECN publicatie:
Titel:
Hydrogen kinetics in crystalline silicon - PECVD SiN studies in mc and Cz silicon
 
Auteur(s):
Hahn, G.; Schönecker, A.; Burgers, A.R.; Ginige, R.; Cherkaoui, K.; Karg, D.
 
Gepubliceerd door: Publicatie datum:
ECN Zonne-energie 1-6-2005
 
ECN publicatienummer: Publicatie type:
ECN-RX--05-018 Conferentiebijdrage
 
Aantal pagina's: Volledige tekst:
4 Download PDF  (87kB)

Gepresenteerd op: 20th European Photovoltaic Solar Energy Conference and Exhibition, Barcelona, Spain, 6-10 juni 2005.

Samenvatting:

Trapping of hydrogen during diffusion in silicon due to impurities and/or other defects is a well known

fact. Using SIMS we can demonstrate that high amounts of oxygen can significantly slow down diffusion of

deuterium originating from PECVD SiN layers after a firing step (NH3 exchanged by ND3) in mc RGS Si. The

slowed down diffusion results in unwanted longer passivation times and lower carrier lifetimes during solar cell

processing. Experiments using Cz Si samples differing in oxygen content are presented as well. High temperature

annealing steps generate O-precipitates of defined size and concentration, and more pronounced trapping of

deuterium appears for higher oxygen concentration. Even more trapping can be detected when O-precipitates are

generated, with the highest deuterium concentrations for large precipitates. An O-depleted region near the surface is

mirrored by lower deuterium concentrations, proving the link between enhanced trapping when oxygen is present.

The overall amount of D-atoms incorporated into the Si bulk after firing can be measured to about 1A1014 cm-2.