Publicaties

Skip Navigation Links.
Recent verschenen
Collapse per documenttypeper documenttype
Expand ECN rapportECN rapport
Expand Boek(hoofdstuk)Boek(hoofdstuk)
Expand Artikel vakbladArtikel vakblad
Collapse Artikel wetenschap tijdschriftArtikel wetenschap tijdschrift
2018
2017
2016
2015
2014
2013
2012
2011
2010
2009
2008
2007
2006
2005
2004
2003
2002
2001
2000
1999
1998
1997
1995
Expand ConferentiebijdrageConferentiebijdrage
Expand PresentatiePresentatie
Expand OverigOverig
Expand Externe notitieExterne notitie
Expand BrochureBrochure
Expand per Unitper Unit
Expand per Clusterper Cluster

Zoeken naar publicaties:
Beperk het zoeken tot de velden:

ECN publicatie:
Titel:
Cost-effective MC-Si cell processing by screenprinting on remote-PECVD layers
 
Auteur(s):
Soppe, W.J.; Weeber, A.W.; Moor, H.H.C. de; Sinke, W.C.; Lauinger, T.; Auer, R.; Lenkeit, B.; Aberle, A.G.
 
Gepubliceerd door: Publicatie datum:
ECN Zonne-energie 1998
 
ECN publicatienummer: Publicatie type:
ECN-RX--98-039 Artikel wetenschap tijdschrift
 
Aantal pagina's:
5  

Gepubliceerd in: Paper, presented at the 2nd World conference and exhibition on photovoltaic solar energy conversion, Vienna, Austria, 06-10 July (), , , Vol., p.-.

Samenvatting:
Silicon nitride (SiN) deposited in a remote-PECVD system has been appliedas AR layer on 10x10 cm2 multicrystalline Si cells in an industrial process using screenprinting on, and 'firing through' the AR coating. It is shown that this deposition process induces an efficient surface and bulk passivation of the solar cells, leading to an absolute efficiency improvement of about 1% when compared with a process sequence in which APCVD TiO2 is deposited after metallization. The best cell of the remote-PECVD SiN group has a Voc of 608 mV, a Jsc of 32.8 mA/cm2 and an efficiency of 14.3%. The efficiency improvement by applying remote-plasma SiN is due to both an enhanced lifetime of the minority charge carriers in the bulk and a reduced recombination at the front surface. Spectral response measurements reveal an increase of the internal quantum efficiency across the whole wavelength range if remote-plasma SiN is applied instead of APCVD TiO2. The increase of the blue response, i.e. the reduction of the front surface recombination, is remarkably high if we take into account that (a) the absorption of SiN in this wavelength region is significantly higher than for TiO2, and (b) the emitters used in this study are characterized by a rather high P concentration at the surface. The importance of these results is that they prove for the first time that it is possible to insert homogeneous SiN deposition by remote-PECVD on 10x10 cm2 and larger wafers in an industrial processing scheme using screenprinting for front and rear side metallization. 5 refs.