Publicaties

Skip Navigation Links.
Recent verschenen
Collapse per documenttypeper documenttype
Expand ECN rapportECN rapport
Expand Boek(hoofdstuk)Boek(hoofdstuk)
Expand Artikel vakbladArtikel vakblad
Expand Artikel wetenschap tijdschriftArtikel wetenschap tijdschrift
Collapse ConferentiebijdrageConferentiebijdrage
2018
2017
2016
2015
2014
2013
2012
2011
2010
2009
2008
2007
2006
2005
2004
2003
2002
2001
2000
1999
1997
1996
1995
1993
1992
1991
1990
Expand PresentatiePresentatie
Expand OverigOverig
Expand Externe notitieExterne notitie
Expand BrochureBrochure
Expand per Unitper Unit
Expand per Clusterper Cluster

Zoeken naar publicaties:
Beperk het zoeken tot de velden:

ECN publicatie:
Titel:
Screen-printed ribbon growth on substrate solar cells exceeding 12% efficiency
 
Auteur(s):
Seren, S.; Hahn, G.; Huster, F.; Kopecek, R.; Gutjahr, A.; Burgers, A.R.; Schönecker, A.
 
Gepubliceerd door: Publicatie datum:
ECN Zonne-energie 1-6-2005
 
ECN publicatienummer: Publicatie type:
ECN-RX--05-019 Conferentiebijdrage
 
Aantal pagina's: Volledige tekst:
4 Download PDF  (1728kB)

Gepresenteerd op: 20th European Photovoltaic Solar Energy Conference and Exhibition, Barcelona, Spain, 6-10 juni 2005.

Samenvatting:

Ribbon Growth on Substrate (RGS) solar cells have been processed at the University of Konstanz using an adapted industrial-type fire-through SiN process. Efficiencies above 12% have been reached on 5x5 cm2 cells processed from boron doped RGS material and efficiencies of 11% from gallium doped RGS material. These are the highest efficiencies obtained on this promising and cost-effective material using an industrial-type cell process. An important factor for the increase in efficiency is the reduced oxygen concentration of almost an order of magnitude in the current RGS wafer material compared to former RGS material. Enhanced Jsc, Voc, especially in case of the gallium doped RGS material, and Leff values in the range of 100 um as well as lifetimes above 4 us demonstrate the potential of the new low oxygen RGS materials. No additional bulk passivation steps have to be performed, a sufficient pasivation is guaranteed solely by hydrogen originating from a hydrogen rich SiNx antireflective coating 1 mA/cm2 enabling efficiencies close to 13% using material of current quality.