Titel:
|
|
Bulk hydrogeneration in mc-Si by PECVD SiNx deposition using direct and remote plasma
|
|
|
|
Auteur(s):
|
Herzog, B.; Hahn, G.; Hofmann, M.; Romijn, I.G.; Weeber, A.W.
|
|
|
|
Gepubliceerd door:
|
Publicatie datum:
|
|
ECN
Zonne-energie
|
3-10-2008
|
|
|
|
ECN publicatienummer:
|
Publicatie type:
|
|
ECN-M--08-065
|
Conferentiebijdrage
|
|
|
|
Aantal pagina's:
|
Volledige tekst:
|
|
4
|
Download PDF
(1770kB)
|
Gepresenteerd op: 23rd European Photovoltaic Solar Energy Conference and Exhibition, Valencia, Spain, 1-5 september 2008.
Samenvatting:
Our investigation focuses on the effect of bulk hydrogenation in mc-Si via PECVD SiNx deposition at low temperatures, so without a subsequent firing step. In a recent publication we have shown that bulk lifetime improvement in mc-Si takes place during PECVD SiNx deposition at 450°C in a PECVD furnace with direct plasma and low plasma generator frequency. In this work we study the bulk hydrogenation of mc-Si during SiNx deposition in different PECVD systems with direct and remote plasma. Tests were performed on p-type and n-type wafers from mc-Si ingots, p-type String Ribbon wafers and p-type EFG ribbon wafers. Neighbouring and adjacent wafers respectively are used to compare bulk lifetimes after single and double sided SiNx deposition on wafers as grown and after P-gettering. Bulk lifetime was measured spatially resolved with µ-PCD. Surface passivation was provided with an iodine-ethanol solution. Significant bulk lifetime improvement in mc-Si takes place during SiNx deposition at low temperatures in PECVD systems with direct and remote plasma, without additional firing step. The effect varies for different mc-Si materials, however, a general statement for all mc-Si materials is difficult.