Titel:
|
|
Efficiency potential of solar cells based on compensated multicrystalline silicon material
|
|
|
|
Auteur(s):
|
|
|
|
|
|
Gepubliceerd door:
|
Publicatie datum:
|
|
ECN
Zonne-energie
|
6-9-2010
|
|
|
|
ECN publicatienummer:
|
Publicatie type:
|
|
ECN-M--10-014
|
Conferentiebijdrage
|
|
|
|
Aantal pagina's:
|
Volledige tekst:
|
|
5
|
Download PDF
(409kB)
|
Gepresenteerd op: 25th European Photovoltaic Solar Energy Conference and Exhibition - 5th World Conference on Photovoltaic Energy Conversion, Valencia, Spain, 6-10 september 2010.
Samenvatting:
The purpose of the present work is evaluation of the impact of Cr-contamination on solar cell properties of compensated multicrystalline silicon (mc-Si) ingots. Cr is an effective recombination centre of practical relevance. Studying its effects in compensated material allows monitoring the dependence of solar cell characteristics on resistivity. Therefore, two compensated materials were investigated: with and without addition of 20 ppm wt Cr to the high-purity Si feedstock. Lifetime measurements on as-cut wafers showed more than one order of magnitude decrease in case of Cr-containing samples. Solar cell manufacturing was accomplished for p-type wafers utilizing two different emitter sheet resistances and a conventional industrial screen-print process. It was found that gettering and hydrogenation involved in cell processing significantly improved material properties in the presence of Cr. As a result cell performance was comparable to the compensated reference. Efficiencies of p-type cells in the range of 15.7% were achieved for this heavily Cr-contaminated, compensated mc-silicon of a resistivity of 4 Ohm.cm.
Terug naar overzicht.